Synthesis and characterization of magnetic
nanoparticles
邱星屏
【期刊名称】《中国化学（英文版）》 【年(卷),期】2000(018)006
【摘要】Magnetic nanoparticles with average diameter in the range of 6.4-8.3 nm have been synthesized by a chemical co-precipi-tation of Fe(Ⅱ) and Fe(Ⅲ) salts in 1.5 M NH4OH solution.The size of the magenetic particles is dependent on both temperature and the ionic strength of the iron ion solutions. The magnetic particles formed at higher temperature or lower ionic strength were slightly larger than those formed at lower temperature or higher ionic strength respectively. In spite of the different reaction co nditions, all the resultant nanopar ticles are nearly spherical and have a similar crystalline structure. At300 K, such prepared nanoparticles are superparamagnetic. The saturation magnetizations for 7.8 and 6.4 nm particles are 71 and 63 emu/g respectively, which are only -20-30% less than the saturation magnetization (90 emu/g) of bulk Fe3O4. Our results indicated that a control of the reaction conditions could be used to tailor the size of magnetic nanoparticles in free precipita tion. 【总页数】4页(834-837)
【关键词】Magne tic particle;magnetite;co-porecipitation
Synthesis and characterization of magnetic nanoparticles