用非比例试样获取比例试样断后伸长率的方法
王俊;王玉玲;张齐;汪静
【期刊名称】《理化检验-物理分册》 【年(卷),期】2009(045)007
【摘要】On the basis of that the plasticity elongation was equal for the unit length in the process of metallic materials uniform deformation, and the constriction occurred in local length, a new method was builded to acquire the percentage elongation after fracture of standard proportional sample, a short sample whose gauge length was shorter than the standard proportional sample's was used in the method. After test, the percentage elongation after fracture which was acquired by means of the method was almost identical with that acquired by means of the method provided by GB/T 228-2002.%根据金属材料均匀塑性变形阶段单位长度塑性伸长相同,以及颈缩变形只在局部长度内发生这一规律,建立了一种用标距小于标准比例试样标距的非标准试样获得标准比例试样断后伸长率的方法.经过试验验证,用该方法测得的断后伸长率与GB/T 228-2002标准规定的方法获得的伸长率相吻合. 【总页数】3页(417-419)
【关键词】断后伸长率;拉伸试验;拉伸试样 【作者】王俊;王玉玲;张齐;汪静
【作者单位】北京星航机电设备厂,理化检测中心,北京,100074;北京航空航天大学,材料科学与工程学院,北京,100083;北京星航机电设备厂,理化检测中心,北
京,100074;北京星航机电设备厂,理化检测中心,北京,100074 【正文语种】中文 【中图分类】TB302.3 【相关文献】
1.冷轧薄钢板拉伸试样尺寸对断后伸长率和最大力总伸长率影响的对比 [J], 罗五四
2.C级钢拉伸试样的屈服现象及断后伸长率的可比性 [J], 王磊 3.SG30钢两种比例拉伸试样伸长率关系的确定 [J], 董秀文 4.断后伸长率换算新方法 [J], 陈升缓
5.金属拉伸试验断后伸长率A的测定方法探讨 [J], 王勇; 陶志刚; 石丽; 刘洋
以上内容为文献基本信息,获取文献全文请下载