DC51D＋AZ热镀铝锌薄板弯曲折痕缺陷的形成原因
王银军;刘学伟;彭琼瑶;彭雄奇
【期刊名称】《机械工程材料》 【年(卷),期】2012(036)012
【摘要】DC51D＋AZ热镀铝锌薄板弯曲成形时出现了弯曲折痕缺陷，对正常产品和缺陷产品的化学成分、组织和性能进行对比分析以找出缺陷产生的原因。结果表明：较低温度的终轧、卷取工艺导致薄板晶粒细化、硬度增高、屈服伸长率增大、塑性变形的稳定性变差是导致产生弯曲折痕缺陷的主要原因。建议钢板生产厂家生产DC51D＋AZ热镀铝锌薄板时应采用较高温度的终轧、卷取工艺和充分的退火。?nding creases appeared on the I)C51D-J-AZ hot-dip A1-Zn alloy coating thin plate in the process of bending forming. Chemical composition, microstructure and mechanical properties of normal product were contracted with those of defective product in order to find the causes of the defects. The results show that lower ultimate roiling temperature and coiling temperature were the main reasons for the defects because they refined the grain size of the thin plate, increased the hardness and the yield elongation and reduced the stability o{ plastic deformation. Consequently, it is proposed that the manufacturer raise ultimate rolling temperature and coiling temperature and enough annealing to produce the DC51D+AZ hot-dip A1-Zn alloy coating thin plate.
【总页数】4页(98-100,104)
【关键词】热镀铝锌薄板;弯曲折痕;缺陷 【作者】王银军;刘学伟;彭琼瑶;彭雄奇
【作者单位】上海梅山钢铁公司技术中心,南京210039;上海梅山钢铁公司技术中心,南京210039;上海交通大学材料科学与工程学院,上海200030;上海交通大学材料科学与工程学院,上海200030 【正文语种】中文 【中图分类】TG142.1 【文献来源】
https://www.zhangqiaokeyan.com/academic-journal-cn_materials-mechanical-engineering_thesis/0201212502889.html 【相关文献】
1.热镀铝锌锌渣缺陷的形成及控制 [J], 曹博蕊
2.热镀铝锌镀层亮点缺陷分析及改进 [J], 刘春富; 张妞妞; 孙伟 3.热镀铝锌产品露钢缺陷治理 [J], 刘春富; 胡红
4.热镀铝锌硅镀层凸点缺陷组织分析及生产工艺优化 [J], 岳崇锋; 江社明; 王银军; 刘昕; 张启富; 曲选辉
5.热镀铝锌钢板表面横向条纹缺陷原因分析及解决方案 [J], 王劲; 林传华; 陈培林; 沈剑峰
以上内容为文献基本信息，获取文献全文请下载
DC51D+AZ热镀铝锌薄板弯曲折痕缺陷的形成原因