多晶硅薄膜低温生长中的表面反应控制
贺德衍
【期刊名称】《物理学报》 【年(卷),期】2001(050)004
【摘要】报道用SiF4和H2的间接微波等离子体化学气相沉积方法低温生长多晶硅(poly-Si)薄膜.实验发现，等离子体中的离子、荷电集团对薄膜生长表面的轰击是影响薄膜结晶质量的重要因素之一.通过外加偏压抑制这些荷电粒子的动能是控制表面生长反应、制备高质量ploy-Si薄膜的有效方法.在合适的外加偏压下制备的poly-Si薄膜，氢含量仅约为0.9 at%，中心位于520?cm-1的Raman特征峰半高宽约为4.4cm-1.%Polycrystalline silicon (poly-Si) thin films were prepared by a remote microwave plasma-enhanced chemical vapor deposition technique at low temperatures using SiF4 and H2 as reactive gases.It was found that the impact of the charged particles in the plasma on the growing surface significantly affects the surface reactions and the crystallinity of the resultant films.By applying the bias on the substrates to decelerate the particles,high-quality poly-Si films, with hydrogen content less than 0.9 at% and the FWHM of 520?cm-1 Raman peak as narrow as 4.4?cm-1,have been obtained at a low temperature of 360℃. 【总页数】5页(779-783)
【关键词】多晶硅薄膜;低温生长;表面生长反应;外加偏压 【作者】贺德衍
【作者单位】兰州大学物理系, 【正文语种】中文 【中图分类】O4 【文献来源】
https://www.zhangqiaokeyan.com/academic-journal-cn_acta-physica-sinica_thesis/0201251065295.html 【相关文献】
1.多晶硅薄膜低温生长中晶粒大小的控制 [J], 黄锐; 林璇英; 余云鹏; 林揆训; 姚若河; 黄文勇; 魏俊红; 王照奎; 余楚迎
2.以SiCl4为源气体用PECVD技术低温快速生长多晶硅薄膜 [J], 黄锐; 林璇英; 余云鹏; 林揆训; 姚若河; 黄文勇; 魏俊红; 王照奎; 余楚迎
3.热丝CVD低温快速生长多晶硅薄膜的研究 [C], 陈官璧; 汪雷; 杨德仁 4.低温快速生长多晶硅薄膜 [C], 黄锐; 林璇英; 姚若河; 黄文勇; 余云鹏; 林揆训; 魏俊红; 余楚迎
5.采用ECR-PECVD技术低温生长多晶硅薄膜 [C], 秦福文; 吴爱民; 王艳艳; 冯庆浩; 李伯海
以上内容为文献基本信息，获取文献全文请下载
多晶硅薄膜低温生长中的表面反应控制