AZ31镁合金薄壁管材挤压技术研究
陈增奎;蒋清;周卫卫;葛东生;马广超
【期刊名称】《精密成形工程》 【年(卷),期】2016(008)003
【摘要】目的：得到综合力学性能良好的AZ31镁合金Φ8 mm薄壁管材。方法研究了热挤压、等温挤压与反向温度场挤压3种工艺对AZ31镁合金薄壁管材晶粒组织和力学性能的影响。结果热挤压管材组织不均匀，头部晶粒粗大、尾部细小，等温挤压和反向温度场管材挤压组织较为均匀。结论反向温度场挤压在模具温度为300℃、坯料温度为20℃条件下，薄壁管材抗拉强度达278 MPa，伸长率达20.1%，综合力学性能最佳。?STRACT:In order to obtain AZ31 alloy thin tubes ofΦ8 mm with good mechanical properties,that focused on the effect of grain microstructure and mechanical properties of the as-extruded thin tubes of AZ31 magnesium alloy by hot extrusion,and un-thermal extrusion. Studies have found that microstructure of hot extrusion is uneven,head grains were coarse,the tail grains were relatively small,and the others were well-proportioned. With comparison of The Three mechanical performance,it got the best tube tensile strength of about 278 MPa,elongation of about 20.1%,when un-thermal extrusion is in the mold temperature of 300℃,billet temperature is 20℃. 【总页数】6页(34-39)
【关键词】热挤压;等温挤压;反向温度场挤压;晶粒组织;力学性能
【作者】陈增奎;蒋清;周卫卫;葛东生;马广超
【作者单位】中国运载火箭技术研究院，北京 100076;首都航天机械公司，北京 100076;北京精密机电控制设备研究所，北京 100076;首都航天机械公司，北京 100076;首都航天机械公司，北京 100076 【正文语种】中文 【中图分类】TG376.9 【文献来源】
https://www.zhangqiaokeyan.com/academic-journal-cn_journal-netshape-forming-engineering_thesis/0201212396479.html 【相关文献】
1.AZ31镁合金薄壁管材等温挤压工艺分析及模具设计 [J], 段亚利; 张治民; 薛勇
2.AZ31镁合金挤压管材力学性能测试 [J], 柴蓉霞; 温莉敏; 许树勤; 池成忠; 范亚地
3.AZ31镁合金管材反向温度场挤压实验研究 [C], YANG Guang; 杨光; JIANG Peng; 蒋鹏; HAN Xiu-zhu; 韩修柱
4.AZ31镁合金管材挤压成型数值模拟与实验研究 [J], 孙颖迪; 陈秋荣 5.AZ31镁合金管材挤压成形数值模拟研究 [J], 李琳琳; 张治民; 薛勇
以上内容为文献基本信息，获取文献全文请下载
AZ31镁合金薄壁管材挤压技术研究