再生骨料透水混凝土力学性能的影响因素研究
王永海;寇卫锋;周永祥;周朋;纪宪坤;王晶
【期刊名称】《工程质量》 【年(卷),期】2015(033)005
【摘要】试验研究了连通孔隙率、聚丙烯纤维、聚合物乳液、颜料及增强料对再生骨料透水混凝土力学性能的影响,结果表明:连通孔隙率越高,透水混凝土强度越低;聚丙烯纤维对再生骨料透水混凝土的抗压强度有一定的提高作用,但是对弯拉强度提高不明显;采用的聚合物乳液降低了再生骨料透水混凝土的抗压强度,对弯拉强度有略微的提高作用;采用的无机增强料对再生骨料透水混凝土的28d抗压强度和弯拉强度提高20%左右;无机颜料对混凝土的强度影响不大;再生骨料透水混凝土可以达到《透水水泥混凝土路面技术规程》CJJ/T 135-2009中透水系数、连续孔隙率、抗压强度、弯拉强度的性能要求.%The effect of porosity,polypropylene fiber,polymer emulsion,pigments and the reinforced material on the mechanical properties of recycled concrete pervious aggregate were investigated,the test results showed that the continuous porosity was higher,strength of the pervious concrete was lower. Polypropylene fiber could improve compressive strength of the recycled aggregate pervious concrete,but the flexural strength increase was not obvious. Polymer emulsion reduced the compressive strength of the recycled aggregate pervious concrete,which had a slightly improved effect on flexural strength.The reinforced material increased the compressive strength and flexural strength of the recycled
aggregate pervious concrete by about 20%;pigment has little effect on strength of concrete;the recycled aggregate pervious concrete could reach the performance requirements of permeable coefficient,the continuous porosity,compressive strength and flexural strength on \135-2009).
【总页数】5页(46-50)
【关键词】再生骨料透水混凝土;强度;孔隙率;聚丙烯纤维 【作者】王永海;寇卫锋;周永祥;周朋;纪宪坤;王晶
【作者单位】中国建筑科学研究院,北京,100013;北京城建设计发展集团股份有限公司三所,北京,100037;中国建筑科学研究院,北京,100013;北京工业大学,北京,100124;中国建筑科学研究院,北京,100013;中国建筑科学研究院,北京,100013 【正文语种】中文 【中图分类】U455.6 【文献来源】
https://www.zhangqiaokeyan.com/academic-journal-cn_construction-quality_thesis/0201211874680.html 【相关文献】
1.再生骨料透水混凝土力学性能的影响因素研究 [C], 王永海; 周永祥; 周朋; 纪宪坤; 贺阳
2.纤维改性再生骨料透水混凝土力学性能透水性和耐磨性研究 [J], 郭磊; 刘思源;
陈守开; 汪伦焰; 薛志龙
3.骨料表面化学预处理对界面区组分梯度分布和混凝土力学性能的影响Ⅱ:骨料化学预处理对混凝土力学性能的改善 [J], 杨久俊; 董延玲; 海然; 吴科如 4.新型透水钢筋混凝土力学性能及研制方法研究 [J], 丁维华; 宋功业 5.新型透水钢筋混凝土力学性能及研制方法研究 [J], 丁维华; 宋功业
以上内容为文献基本信息，获取文献全文请下载
再生骨料透水混凝土力学性能的影响因素研究