一种简单的模板法制备聚苯乙烯纳米管
宋国君;佘希林;李建江
【期刊名称】《青岛大学学报（工程技术版）》 【年(卷),期】2004(019)002
【摘要】为了制备具有高强度聚苯乙烯纳米管及其阵列结构,以孔径仅有200nm的阳极氧化铝为模板,采用聚合物溶液浸润模板这一简单的物理技术,成功制备了具有常规相对分子质量的聚苯乙烯纳米管及其阵列.SEM和TEM测试结果表明: 聚苯乙烯质量分数分别为2.5%,5.0%和10.0%的聚合物溶液可以制得管壁厚度分别为50 n m,70 nm和80 nm的纳米管.可知聚合物溶液浓度是影响纳米管结构的主要因素之一.计算可知:聚苯乙烯质量分数为10.0%的聚合物溶液完全充满纳米孔时,溶剂挥发后高分子链沉积在孔内壁上形成纳米管的管壁厚度约为5 nm.由此推断出聚合物溶液浸润阳极氧化铝模板的过程反复多次进行,并归纳出溶液浸润模板制备聚合物纳米管的多次浸润机理.%In order to prepare stable mechanical polystyrene(PS)nanotubes and t heir arrays,a solution of normal relative molecular mass PS was filtrated into anodic aluminum oxide(AAO)template with only 200 nm pores.Scanning electron m I croscope (SEM) and transmission electron microscope(TEM) were applied for chara cterizing the structures of PS nanotubes.The results indicated that PS tubules were successfully obtained and the wall thickness of PS tubules prepared by the 2.5%, 5.0% and 10.0% mass fraction of PS solution were respectively 50,70an d 80 nm.The structure of polymer nanotubes depends strongly on the concentratio n of PS
solution.When the polym er solution wets AAO template, a thin polymer film will be formed on the inner p orous wall.The thin film/AAO composite membrane acts as a \repeatedly.According to the multi-time wetting mechanism, P S solution wets template,and then forms polymer nanotubes. 【总页数】6页(24-29)
【关键词】模板法;常规相对分子质量聚苯乙烯;阳极氧化铝;聚合物纳米管;多次浸润机理
【作者】宋国君;佘希林;李建江
【作者单位】北京化工大学材料学院,北京,100029;青岛大学化工学院,山,东,青岛,266071;北京化工大学材料学院,北京,100029;青岛大学化工学院,山,东,青岛,266071 【正文语种】中文 【中图分类】TB383 【文献来源】
https://www.zhangqiaokeyan.com/academic-journal-cn_journal-qingdao-university-engineering-technology-edition_thesis/0201210179227.html 【相关文献】
1.接枝聚苯乙烯的多壁碳纳米管的制备及在聚苯乙烯基体中分散性能的研究 [C], 李艳亮; 沈曾民; 程斌
2.微纳层叠共挤碳纳米管填充高抗冲聚苯乙烯/高抗冲聚苯乙烯
(CNTs+HIPS/HIPS)交替层状复合材料的介电性能 [J], 戴坤添; 安瑛; 王玮鹭; 李莉; 杨卫民; 焦志伟
3.溶液共混法制备聚苯乙烯/多壁碳纳米管复合导电材料 [J], 赵金安
4.细乳液原位聚合法制备聚苯乙烯非共价修饰的碳纳米管 [J], 晋圣松; 唐国强; 王红敏; 边成香; 徐学诚
5.溶液法和熔融法制备聚苯乙烯/碳纳米管复合材料及其性能研究 [J], 王一科
以上内容为文献基本信息，获取文献全文请下载
一种简单的模板法制备聚苯乙烯纳米管