多级孔 Zn-La／HZSM-5制备及在甲醇芳构化中的应用
孙志岩;赵伟林;胡志君;张玲;赵岑;王海彦
【期刊名称】《石油化工高等学校学报》 【年(卷),期】2013(000)005
【摘要】采用NaO H溶液对ZSM-5分子筛进行碱处理，制备了多级孔径ZSM-5分子筛。采用浸渍法制备了多级孔Zn-La/HZSM-5分子筛，并采用XRD、BET、SEM和N H3-T PD等方法进行了表征，在固定床反应器中进行甲醇芳构化反应。结果表明，经过碱处理，ZSM-5分子筛的平均孔径、孔容和比表面积增大，孔径呈微孔和介孔多级孔分布。Zn和La的负载量均为0．5％时，Zn-La/ZSM-5分子筛具有较好的芳构化活性。在反应温度475℃、反应压力0．6 MPa、空速（LHSV）0．8 h-1条件下，芳烃（苯、甲苯和二甲苯）的收率可达32．3％。%The alkaline treatment of ZSM-5 zeolite with NaOH solution ,received the hierarchical porous ZSM-5 zeolite ,Zn and La by co-impregnation method of loading in the alkali treatment of the modified ZSM-5 zeolite ,the ZSM-5 molecular sieves were characterized by XRD ,BET ,SEM and NH3-TPD .The reaction of methanol aromatization was investigated in a fixed bed reactor .The results show that after alkali treatment modified ZSM-5 zeolite had a pore size increased and the acidity distribution was changed;Zn-La/HZSM-5 zeolite had the better catalytic ,Zn and La with the load capacity of each of 0 .5% , the reaction temperature was 475 ℃ ,the reaction pressure was 0 .6 MPa ,LHSV was 0 .8 h-1 ,the yield of aromatic hydrocarbons
(benzene ,toluene and xylene) up to 32 .3% . 【总页数】5页(23-26,32)
【关键词】多级孔;ZSM-5分子筛;甲醇;芳构化;锌;镧 【作者】孙志岩;赵伟林;胡志君;张玲;赵岑;王海彦
【作者单位】辽宁石油化工大学化学化工与环境学部，辽宁抚顺 113001;中国石油抚顺石化公司石油二厂，辽宁抚顺113004;中国石油抚顺石化公司石油二厂，辽宁抚顺113004;辽宁石油化工大学顺华能源学院，辽宁抚顺113001;辽宁石油化工大学化学化工与环境学部，辽宁抚顺 113001;辽宁石油化工大学化学化工与环境学部，辽宁抚顺 113001 【正文语种】中文
【中图分类】TE624.4+8;TQ426.82 【文献来源】
https://www.zhangqiaokeyan.com/academic-journal-cn_journal-petrochemical-universities_thesis/0201210538122.html 【相关文献】
1.Zn、Ga改性多级孔ZSM-5分子筛的原位合成及甲醇芳构化催化性能 [J], 蒋忠祥; 王海彦; 张玲; 魏民; 孙悦
2.碱改性对甲醇芳构化催化剂Zn/La-HZSM-5性能的影响 [J], 段超; 张睿; 谢小莉; 王红梅; 潘蕊娟; 齐小峰
3.Zn对HZSM-5分子筛催化剂物化及甲醇芳构化反应性能的影响 [J], 刘维桥; 雷卫宁; 尚通明; 李卫华; 周全法; 王恒强; 任杰
4.活性氢物质甲醇存在时噻吩在La/HZSM-5 催化剂上的转化反应研究 [J], 罗
立文; 李虎; 夏道宏; 吴超波; 张宏伟
5.多级孔HZSM-5分子筛催化剂的制备及低碳烃芳构化应用 [J], 张瑞珍; 王翠; 邢普; 温少波; 王剑; 赵亮富; 李玉平
以上内容为文献基本信息，获取文献全文请下载
多级孔 Zn-La／HZSM-5制备及在甲醇芳构化中的应用