纳米镍修饰TiO2纳米管电极检测胰岛素
张云怀;董西哲;肖鹏;何辉超;李小玲
【期刊名称】《应用化学》 【年(卷),期】2012(029)008
【摘要】Highly ordered TiO2 nanotube arrays ( TiO2 NTs) fabricated by anodization were employed as a substrate and loaded with Ni nanoparticles by pulse electrodeposition. Hie morphology and composites of titanium dioxide nanotubes and Ni/TiO2NTs electrodes were investigated using scanning electron microscopy and energy-dispersive X-ray spectroscopy, respectively. The Ni/TiO2 NTs was used as an amperometric detector for electrocatalytic oxidation and determination of insulin. The results show that Ni/TiO2NTs electrode enables the oxidative detection of insulin at this modified electrode. The linear dynamic range of the detection is 0. 8 ~ 1.6 μmol/L in 0. 1 moI/L NaOH electrolyte, with a good sensitivity (0. 49 ×10-3 A/(μmol·L-1·cm-2) and low detection limit (0. 28 μmol/L).%采用阳极氧化法制备出高度有序的TiO2纳米管阵列作为基础电极,通过电沉积法将纳米镍颗粒负载在基础电极上,从而制备了纳米镍-二氧化钛纳米管( Ni/TiO2NTs)修饰电极.分别采用扫描电子显微镜和X射线衍射对Ni/TiO2NTs电极的形貌及组分进行了表征.将Ni/TiO2NTs电极用于对胰岛素的电化学测定.结果表明,在0.1mol/L NaOH支持电解液中,胰岛素在Ni/TiO2 NTs电极上有较好的电化学响应,胰岛素浓度在0.8～1.6 μmol/L范围内,峰电流密度与其浓度呈良好的线性关系,检测限为0.28
μmol/L,灵敏度为0.49×10-3 A/( μnol·L-1·cm-2). 【总页数】6页(948-953)
【关键词】电化学;修饰电极;纳米镍;TiO2纳米管阵列;胰岛素 【作者】张云怀;董西哲;肖鹏;何辉超;李小玲
【作者单位】重庆大学化工学院 重庆400030;重庆大学化工学院 重庆400030;重庆大学物理学院 重庆400030;重庆大学化工学院 重庆400030;重庆大学化工学院 重庆400030 【正文语种】中文 【中图分类】O646 【文献来源】
https://www.zhangqiaokeyan.com/academic-journal-cn_chinese-journal-applied-chemistry_thesis/0201272091744.html 【相关文献】
1.NiAl-LDH修饰TiO2纳米管电极对葡萄糖的检测 [J], 郑鑫才; 刘东斌; 申延明
2.NiAl-LDH修饰TiO2纳米管电极对葡萄糖的检测 [J], 郑鑫才; 刘东斌; 申延明
3.CsPW11Fe/TiO2纳米管修饰电极的制备及对H2O2的检测 [J], 黄燕霞; 章金明; 黄彦卿; 王崇太; 华英杰
4.碳纳米管/纳米TiO2复合膜电极与纳米TiO2电极电化学性能比较 [J], 张金花; 张莉艳
5.碳纳米管/纳米TiO2复合膜修饰电极的制备及其对马来酸的电催化还原 [J],
张金花; 褚道葆
以上内容为文献基本信息，获取文献全文请下载
纳米镍修饰TiO2纳米管电极检测胰岛素