实验三:电偶腐蚀速度的测定
一、 试验目的:
1.掌握电偶腐蚀测试原理;
2.掌握电极电位、耦合电流的测量方法; 3.掌握实验分析方法。
二、实验原理:
当两种金属或合金相接触在溶液中可以发现在该液中电,位较负的金属腐蚀速度加大,而电位较正的金属受到保护,这种现象就是电偶腐蚀。金属或合金制成电极,应用电偶腐蚀计测量,便可测定其各个电极开路电位,耦合电位,回路电流等值。 三、仪器药品
电偶腐蚀计,金属电极(Fe,紫铜,黄铜),饱和甘汞电极,烧杯,量筒,天平 砂纸,滤纸,酒精棉,pH试纸,NaCl, 四、实验内容及步骤
1. 将各电极用水砂纸打磨光亮,用酒精棉擦干待用; 2. 配制100毫升3%NaCl溶液,连接电偶腐蚀计线路;
3. 测定各电极在3%NaCl溶液中相对于石墨电极的自腐蚀电位,填入表格; 4. 测Fe-紫铜和黄铜-紫铜电偶电流随时间的变化
待电极自腐蚀电位稳定后接通电路,测定电偶电流随时间的变化情况,直到电流比较稳定时为止,测量耦合电极相对于参比电极的电位。电偶电流最初随时间变化较快,可适当缩小记录时间间隔,15秒或半分钟计一次数。 五、实验数据及结果处理
1. 所有测量数据记录于表格中
自腐蚀电位:Fe:-0.595V 黄铜:-0.208V 紫铜:-0.192V 耦合电位: Fe-紫铜:-0.552V 黄铜-紫铜:-0.218V Fe-紫铜电偶电流随时间变化
t/s12345678910111213141516171819202122232425262728293031323334353637383940414243444546474849505152535455565758596061626364656667686970717273747576777879600602604606608610Ig(Fe-Cu)/mA154.9131.8121.4111.2100.493.788.38279.277.9757268.366.86462.961.659.558.156.855.354.352.65251.249.848.948.347.847.146.245.144.54443.242.942.241.441.140.540.339.138.638.3383837.937.23736.335.635.535.134.934.434.83433.533.433.433.332.532.532.332.131.832.23231.231.630.330.230.229.729.929.629.329.329.219.819.819.819.819.820.1t/s8081828384858687888990919293949596979899100101102103104105106107108109110111112113114115116117118119120121122123124125126127128129130131132133134135136137138139140141142143144145146147148149150151152153154155156157158159590592594596598Ig(Fe-Cu)/mA29.128.728.528.428.528.328.12827.928.127.927.928.127.227.627.827.427.327.127.526.426.426.526.426.426.226.226.426.325.826.126.125.625.625.625.425.625.425.325.225.225.525.22524.824.824.725.124.624.624.624.524.624.424.524.524.324.324.224.224.124.424.42423.723.623.823.623.623.623.523.623.523.523.523.523.423.523.423.419.920.219.819.919.8t/s160161162163164165166167168169170171172173174175176177178179180181182183184185186187188189190191192193194195196197198199200201202203204205206207208209210211212213214215216217218219220221222223224225226227228229230231232233234235236237238239580582584586588Ig(Fe-Cu)/mA23.423.223.223.223.223.523.223.222.922.922.922.922.922.922.922.823.222.823.22322.72322.722.72322.722.622.622.722.622.622.622.622.622.622.622.622.622.622.722.722.622.622.622.922.722.922.62322.722.922.922.722.922.722.722.722.723232322.722.722.723232322.7232322.7232322.722.922.722.922.722.922.720.120.120.320.220.2 t/s240242244246248250252254256258260262264266268270272274276278280282284286288290292294296298300302304306308310312314316318320322324326328330332334336338340342344346348350352354356358360362364366368370372374376378380382384386388390392394396398570572574576578Ig(Fe-Cu)/mA22.922.922.722.622.622.622.622.622.622.622.622.622.622.622.622.622.622.722.722.822.82323.223.523.62423.824.324.524.624.925.225.225.626.125.926.326.526.626.927.127.627.327.427.427.427.427.827.427.527.527.627.627.527.627.627.627.627.527.527.327.327.227.52726.626.526.526.526.426.426.226.226.225.925.925.726.125.925.620.420.220.220.220.2t/s400402404406408410412414416418420422424426428430432434436438440442444446448450452454456458460462464466468470472474476478480482484486488490492494496498500502504506508510512514516518520522524526528530532534536538540542544546548550552554556558560562564566568Ig(Fe-Cu)/mA25.625.525.425.425.225.22524.824.825.124.624.624.524.624.524.324.224.524.423.823.823.623.623.523.523.523.523.423.223.42322.922.822.82322.622.622.622.522.522.522.422.322.222.222.422.222.222.222.221.921.821.821.821.822.121.921.821.621.521.621.721.521.421.521.321.321.221.221.221.521.420.620.620.620.620.620.620.520.520.520.420.520.420.4黄铜-紫铜电偶电流随时间变化
t/s12345678910111213141516171819202122232425262728293031323334353637383940414243444546474849505152535455565758596061626364656667686970717273747576777879808182838485Ig(Cu-Cu)t/s3.53.43.33.13.12.92.82.72.72.92.52.62.52.52.52.52.52.52.42.52.52.52.42.42.42.42.42.42.42.42.42.42.42.42.42.42.42.42.32.22.22.22.22.22.22.22.22.22.22.22.22.22.22.22.22.22.22.22.22.22.22.22.32.32.32.32.32.32.32.32.32.32.32.32.32.32.32.32.32.32.32.32.32.32.38687888990919293949596979899100101102103104105106107108109110111112113114115116117118119120121122123124125126127128129130131132133134135136137138139140141142143144145146147148149150151152153154155156157158159160161162163164165166167168169604Ig(Cu-Cu)/t/s2.32.32.32.32.32.32.32.32.32.32.32.32.32.32.32.32.32.32.32.32.32.32.32.32.32.32.32.32.32.32.32.32.32.32.32.32.32.32.32.32.32.32.32.32.32.32.32.32.32.32.32.32.32.32.32.32.32.32.32.42.42.42.42.42.42.42.42.42.42.42.42.42.42.42.42.42.42.42.42.42.42.42.42.42170171172173174175176177178179180181182183184185186187188189190191192193194195196197198199200201202203204205206207208209210211212213214215216217218219220221222223224225226227228229230231232233234235236237238239240242244246248250252254256258260262264266606Ig(Cu-Cu)/t/s2.42.42.42.42.42.52.52.52.52.52.52.52.52.52.52.52.52.52.52.52.52.52.52.52.52.52.52.52.52.52.52.52.52.52.52.52.52.52.52.52.52.52.52.52.52.52.52.52.52.52.52.52.52.52.52.52.52.52.52.52.52.52.52.52.52.52.52.52.52.52.52.52.52.52.52.52.52.52.52.52.52.52.52.52268270272274276278280282284286288290292294296298300302304306308310312314316318320322324326328330332334336338340342344346348350352354356358360362364366368370372374376378380382384386388390392394396398400402404406408410412414416418420422424426428430432434608Ig(Cu-Cu)/t/s2.52.52.52.52.52.62.62.62.62.62.62.62.62.62.62.62.62.62.62.62.62.62.52.52.52.52.52.52.52.52.52.52.52.52.52.52.52.52.52.52.52.52.52.52.52.42.42.42.42.42.42.42.42.42.42.42.42.42.42.42.42.42.42.32.22.22.22.22.22.22.22.22.22.22.22.22.22.22.22.12.12.12.12.12436438440442444446448450452454456458460462464466468470472474476478480482484486488490492494496498500502504506508510512514516518520522524526528530532534536538540542544546548550552554556558560562564566568570572574576578580582584586588590592594596598600602610Ig(Cu-Cu)/mA2.12.12.12.12.12.12.12.12.12.12.12.12.12.12.12.12.12.12.12.12.12.12.12.12.12.12.12.12.12.12.12.12.12.12.12.12.12.12.12.12.12.12.12.12.12.12.12.12.12.12.12.12.12.12.12.22.22.22.22.22.22.22.22.22.22.222222222222222222222. 将Fe-紫铜和黄铜-紫铜电偶电流随时间的变化绘制在同一张图中;
Ig(Fe-Cu) Ig(Cu-Cu)1601401201008060402000100200300400500600700Ig/mAt (s)
3. 结果及讨论
1. 测量个电极开路电位时,其电位一直浮动不定,这是由于金属表面的极化和由
于阴、阳极反应生成表面膜或腐蚀产物的影响。
2. 两金属电极电位差越大,其测量电流Ig越大,试验中Fe-紫铜电偶为-0.552V,
大于紫铜-黄铜电偶的耦合电位,所以其测量的Ig也大于后者。
3. 随着反应的进行,Ig均随时间而减小,反应初始时Ig下降迅速,之后,随着
极化的进行,由于电极外侧生成钝化膜等原因,电流都逐渐减小,之后趋于平稳,中间也有波动起伏的过程。
4. 电极是否打磨干净会影响试验中电流的稳定和大小,但整体Ig-t变化趋势不变。
参考文献
1、《实验电化学》王圣平 编 中国地质大学出版社 2、《腐蚀电化学原理》第一版 曹楚南 编