g-C3N4纳米管的制备及其光催化降解性能
王晓雪;高建平;赵瑞茹;吴永利;郝超月;邱海霞
【期刊名称】《无机化学学报》 【年(卷),期】2018(034)006
【摘要】以三聚氰胺和碳酸氢铵混合物为原料,采用简便热解法制备g-C3N4纳米管.热解过程中碳酸氢铵分解释放出大量的NH3,能够诱导纳米管的形成.利用X射线衍射(XRD)、扫描电子显微镜(SEM)、红外光谱(IR)、N2吸附-脱附、紫外-可见漫反射光谱以及紫外可见光谱(UV)等分析测试方法对该光催化剂的微观形貌结构和催化性能进行了表征.以罗丹明光催化降解为模型反应研究了g-C3N4纳米管的光催化活性.g-C3N4纳米管的表面积明显增大,且能够有效地促进光生电子转移,在可见光下具有较强的光催化性能,降解率在60和120 min时分别能达到95％和99.4％,且循环重复利用5次后降解率不低于92％.%g-C3N4 nanotubes were prepared by pyrolysis of a mixture of melamine and ammonium bicarbonate via a simple and convenient method.The morphology and catalytic properties of the photocatalysts were characterized by X-ray diffraction (XRD),scanning electron microscopy (SEM),infrared spectroscopy (IR),N2 adsorptiondesorption,ultraviolet-visible diffuse reflectance spectroscopy and UV-visible spectroscopy.The photocatalytic activity of g-C3N4 nanotubes to rhodamine B degradation was investigated.The photocatalytic activity of the g-C3N4 nanotubes under the visible light irradiation was effectively promoted because the tube structure can effectively promote the photo-electron
transfer.The degradation percentage of rhodamine B was 95 and 99.4％ at 60 and 120 min respective.The g-C3N4 nanotubes also displayed high recyclability.
【总页数】6页(1059-1064)
【关键词】g-C3N4;纳米管;光催化;罗丹明B
【作者】王晓雪;高建平;赵瑞茹;吴永利;郝超月;邱海霞
【作者单位】天津大学理学院化学系,天津300350;天津大学理学院化学系,天津300350;天津大学理学院化学系,天津300350;天津大学理学院化学系,天津300350;天津大学理学院化学系,天津300350;天津大学理学院化学系,天津300350
【正文语种】中文 【中图分类】O643.3 【文献来源】
https://www.zhangqiaokeyan.com/academic-journal-cn_chinese-journal-inorganic-chemistry_thesis/0201250686938.html 【相关文献】
1.TiO2纳米管催化剂的制备及其光催化性能 [J], 李荡; 曹晖; 吴林冬; 常飞 2.B掺杂TiO2纳米管的制备及光催化性能研究 [J], 张晓丽; 郭小阳
3.(Ni-Mo)-TiO2纳米薄膜的制备及其光催化降解罗丹明B的性能 [J], 李爱昌; 赵娣; 李倩; 张敬; 郑彦俊
4.介孔TiO2空心纳米球的制备及光催化降解性能研究 [J], 葛成海; 靳长清; 坚增运; 魏永星; 许岗
5.Pt负载型二氧化钦纳米管/纳米晶复合光催化剂的制备及其光催化性能 [J], 余威威; 张青红; 石国英; 李耀刚; 王宏志
以上内容为文献基本信息，获取文献全文请下载
g-C3N4纳米管的制备及其光催化降解性能